ISO-9015-2 › Destructive tests on welds in metallic materials - Hardness testing - Part 2: Microhardness testing of welded joints
The following bibliographic material is provided to assist you with your purchasing decision:
ISO 9015-2:2016 specifies microhardness testing on transverse sections of welded joints of metallic materials with high hardness gradients. It covers Vickers hardness tests in accordance with ISO 6507‑1, normally with test loads of 0,98 N to less than 49 N (HV 0,1 to less than HV 5).
NOTE Testing ensures that the highest and/or the lowest level of hardness of both parent materials (in the case of dissimilar materials both parent materials) and weld metal is determined.
ISO 9015-2:2016 is not applicable to hardness testing of welds with loads of 49,03 N and above, which is covered by ISO 9015‑1.
ISO 9015-2:2016 is not applicable to Vickers hardness testing of resistance spot, projection and seam welds, which is covered by ISO 14271.
This part of ISO 9015 is not applicable to hardness testing of very narrow welds, e.g. those typically produced by laser and electron beam welding (see ISO 22826).
To find similar documents by classification:
This document comes with our free Notification Service, good for the life of the document.
This document is available in either Paper or PDF format.
Customers who bought this document also bought:
ASTM-A182Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service
ASTM-A668
Standard Specification for Steel Forgings, Carbon and Alloy, for General Industrial Use
ASTM-A473
Standard Specification for Stainless Steel Forgings
Document Number
ISO 9015-2:2016
Revision Level
2ND EDITION
Status
Current
Publication Date
Jan. 1, 2016
Committee Number
ISO/TC 44/SC 5